GRADE		% C	% Si	% Mn	% P	% S	% Ni	% Cr	% Cu	Others	Comparison		Application
AISI	DIN	MAX	MAX	MAX *	MAX	MAX *					B.S.	JIS
201		0.15	1	7.00 - 9.00	0.1	0.03	0.40 - 1.00	14.00 - 16.00	1.50 - 2.50			SUS 201	Furniture and decorative items, baskets & architectural products.
202		0.15	1	7.50 - 10.00	0.06	0.03	4.00 - 6.00	17.00 - 19.00	1.50 - 2.50			SUS 202	Shafts, Grills and Racks
204 Cu	1.4597	0.09	1	6.50 - 8.50	0.06	0.03	1.50 - 3.00	16.00 - 17.00	2.00 - 3.00			SUS 204Cu	Shafts, Grills and Racks
302	1.4312	0.15	1	2	0.045	0.03	8.00 - 10.00	17.00 - 19.00			302S25	SUS 302	Precision Components & Shafts
303	1.4305	0.15	1	2	0.2	0.15 - 0.30	8.00 - 10.00	17.00 - 19.00		Mo = 0.60 max	303S31	SUS 303
303 Cu		0.15	1	2	0.15	0.10 MIN	6.00 - 10.00	17.00 - 19.00		Cu = 2.50 - 4.00	303S30
304	1.4301	0.08	1	2	0.045	0.03	8.00 - 10.50	18.00 - 20.00			304S15	SUS 304	General all purpose, Kitchen Equipments,Food Production facilities
304 L	1.4306	0.03	1	2	0.045	0.03	8.00 - 12.00	18.00 - 20.00		N = 10ppm max	304S11	SUS 304L
310	1.4841	0.25	1.5	2	0.045	0.03	19.00 - 22.00	24.00 - 26.00			310S24	SUH 310	Heat Exchangers, Gas Turbines
310 S	1.4845	0.08	1.5	2	0.045	0.03	19.00 - 22.00	24.00 - 26.00				SUS 310S	Heat Exchangers, Gas Turbines
316	1.4401	0.08	1	2	0.045	0.03	10.00 - 14.00	16.00 - 18.00		Mo = 2.00 - 3.00	316S16	SUS 316	Anticorrosion parts, valves and components in Petro Chemical and Dying Industry.
316 L	1.4404	0.03	1	2	0.045	0.03	10.00 - 14.00	16.00 - 18.00		Mo = 2.00 - 3.00 &	316S11	SUS 316L
										N = 10ppm max
316 Ti	1.4571	0.08	1	2	0.045	0.03	10.00 - 14.00	16.00 - 18.00		Mo = 2.00 - 3.00 &	320S31		Anti Corrosion parts, Car Mufflers
										Ti= 5x(C+N) min to 0.70
321	1.4541	0.08	1	2	0.045	0.03	9.00 - 12.00	17.00 - 19.00		Ti= 5x(C+N) min to 0.70	321S31	SUS 321	Aircraft Engine, Vent Pipes, Heat exchanger
630 / 17-4PH	1.4542	0.07	1	1	0.04	0.03	3.00 - 5.00	15.00 - 17.50					Shafts, Advanced Mold

GRADE		% C	% Si	% Mn	% P	% S	% Ni	% Cr	Others	Comparison		Application
AISI	DIN	MAX	MAX	MAX *	MAX	MAX *				B.S.	JIS
430	1.4016	0.12	1	1	0.04	0.03	0.5	16.00 - 18.00		430S15	SUS430	Kitchen Equipments, Material for Construction
430 F		0.12	1	1.25	0.06	0.15 MIN		16.00 - 18.00			SUS 430F	Components, Nozzle for Fuel Injection
430 F	1.4104	0.10 - 0.17	1	1.5	0.04	0.15 - 0.35	0.5	15.50 - 17.50	Mo = 0.20 - 0.60
1.4105		0.08	1.5	1.5	0.04	0.15 - 0.35		16.00 -18.00	Mo = 0.20 - 0.60

GRADE		% C	% Si	% Mn	% P	% S	% Ni	% Cr	Comparison		Application
AISI	DIN	MAX	MAX	MAX *	MAX	MAX *			B.S.	JIS
403	1.4024	0.15	0.05	1	0.04	0.03		11.50 - 13.00	420S29	SUS 403	Shafts, Shaft keys, OA Devices
410	1.4006	0.15	1	1	0.04	0.03		11.50 - 13.50	410S21	SUS 410	Shafts, Shaft keys, OA Devices
416	1.4005	0.15	1	1.25	0.06	0.15 MIN		12.00 - 14.00	416S21	SUS 416	Machined Components for various industry levels, Various Shafts
420	1.4021	0.15	1	1	0.04	0.03		12.00 - 14.00	420S37	SUS 420J1
420 B	1.4028	0.26 - 0.35	1	1.5	0.04	0.03		12.00 - 14.00	420S45	SUS 420J2
420 C	1.4034	0.43 - 0.50	1	1	0.04	0.03		12.50 - 14.00
431		0.2	1	1	0.04	0.03	1.25 - 2.50	15.00 - 17.00	431S29	SUS 431	Marine shafts, Aircraft parts
431	1.4057	0.12 - 0.22	1	1.5	0.04	0.03	1.50 - 2.50	15.00 - 17.00			Marine shafts, Aircraft parts

Stainless Steel Bolting Material (As Per Astm A19 3 & Astm A320 Specification)

(CARBIDE SOLUTION TREATED & STAIN HARDENED BARS)

Mechanical Requirement (Mpa) (minimum)

GRADE	%C	%Mn	%Si	%P	%S	%Ni	%Cr	SIZE (Inch)	Tensile Strength	0.2% Yield Strength	% ELO	% RA	Hardness BHN
	MAX	MAX	MAX	MAX	MAX
B8 / 304	0.08	2	1	0.045	0.03	8.00-10.5	18.00-20.00	BELOW 3/4"	860	690	12	35	321
Class II								3/4"to1" incl	795	550	15	35	321
								1"to1.1/4" incl	725	450	20	35	321
								1.1/4"to1.12" incl	690	345	28	45	321
B8M / 316	0.08	2	1	0.045	0.03	10.00-14.00	16.00-18.00	BELOW 3/4"	760	665	15	45	321
Class II						%Mo= 2.00-3.00		3/4" to 1" incl	690	550	20	45	321
								1"to1.1/4"incl	655	450	25	45	321
								1.1/4"to1.1/2" incl	620	354	30	45	321
(CARBIDE SOLUTION TREATED)								SIZE (Inch)	Tensile	Yield	%ELO	% RA	HARDNESS
									Strength	Strength			BHN
B8/304 & B8M/316 Class I								ALL SIZES	515	205	30	50	223
A2-70 /								Less than M20	700	450	0.4 D
A4-70								Between M20 - M30	500	250	0.4 D
A4-80								Less than M20	800	600	0.3 D

QUENCHED & TEMPERED ALLOY STEEL

Mechanical Requirement (Mpa) (minimum)

(For Fasteners Application)

GRADE	%C	%Mn	%Si	%P	%S	%Cr	%Mo	Size (in)	Tensile Strength	0.2% Yield Strength	% ELO	% RA	Hardness BHN
				MAX	MAX
B7	0.37-	0.65-	0.15-	0.035	0.04	0.75-1.20	0.15-0.25	upto 2.12" incl	860	720	16	50	321
A193	0.49	1.1	0.35					over 2.12" to 4 incl	795	655	16	50	302
B16	0.36-	0.45-	0.15-	0.035	0.04	0.80-1.15	0.50-0.65	upto 2.12" incl	860	725	18	50	321
A193	0.47	0.07	0.35					upto 2.12" incl	860	725	18	50	321
	% V = 0.25-0.35					%AI=0.015 MAX
L7	0.38-	0.75-	0.15-	0.035	0.04	0.80-1.10	0.15-0.25	upto 2.1/2"incl	860	720	16	50	321
A320	0.48	1	0.35			IMPACT PROPERTIES : Average of Thre=27J Min; One specimen = 20J Min (test Temp.-101°C)
Quenched & Tempered Carbon Steel (For Fasteners Application) As Per Iso-898-1

GRADE	%C	%Mn	%Si	%P	%S	%Cr	%Mo	Size (in)	Tensile Strength	0.2% Yield Strength	% ELO	% RA	Hardness BHN
				MAX	MAX
8.8	0.25-	0.6	-	0.035	0.035	-	-	upto 16.0min incl	800	640	12	-	238-304
	0.55	min						over 16.0 mm	830	660	12	-	342-318
NOTE : We Can Supply Other Property Class of ISO-898-1 Specification									IMPACT PROPERTIES : 30J Min
Spheroidised Annealed + Phosphate Coated & Cold Drawn Ball Bearing Quality Wire / Drawn & Ground Bars

GRADE	%C	%Mn	%Si	%P	%S	%Cr	%Mo	BARS, WIRE SIZE, COIL WEIGHT	Compasiron of International Standard
				MAX	MAX			& MECHANICAL PROPERTIES AS	AISI	DIN	B.S	JIS
SAE	0.98-	0.25-	0.20-	0.025	0.025	0.25	1.30-1.60	PER CUSTOMERS REQUIREMENT
52100	1.1	0.45	0.35					MICRO & INCLUSION RATING AS	52100	100Cr6	534A99	SUJ2
	0=15ppm		%Cu=0.35 MAX			%Mo=		PER ASTM A295 SPECI.	660	12	-	342-318
	0=15ppm		%Cu=0.35 MAX			0.15-0.25		PER ASTM A295 SPECI.	660	12	-	342-318